SCIENCE CHINA Materials•2026•DOI: 10.1007/s40843-026-4267-y
The synthesis of two-dimensional MBenes from MAB-phase ceramics is impeded by uncontrolled etching kinetics that compromise structural integrity and yield. This study introduces a vacuum molten salt strategy to regulate space-charge accumulation during the selective removal of Al from Mo2AlB2, producing honeycomb-like architectures. The vacuum environment suppresses oxidative side reactions and modulates ionic transport, enabling precise control over etching depth and morphology. The resulting Mo2AlB2 exhibits exceptional electromagnetic wave absorption, with a minimum reflection loss of -56.3 dB at 2.4 mm and an effective absorption bandwidth of 6.8 GHz. These metrics surpass conventional etching-derived MBenes by a factor of 2.5 in attenuation capacity. The space-charge-regulated mechanism is elucidated through in situ spectroscopic and computational analyses, revealing that vacancy-induced charge redistribution governs the etching front propagation. This work establishes a scalable route for high-purity MBenes with tailored porosity, addressing critical bottlenecks in energy absorption and catalytic applications. The vacuum molten salt approach eliminates the need for hazardous HF, offering a safer and more environmentally benign pathway for industrial translation.
SCIENCE CHINA Materials•2026•DOI: 10.1007/s40843-026-4322-4
Ultrafast scintillators with low-nanosecond emission are essential for next-generation high-rate X-ray and particle imaging. Although Ce3+-activated scintillators inherently exhibit fast response characteristics, conventional Ce3+-doped hosts rarely achieve low-nanosecond ultrafast decay. Here, we report a high-entropy fluoride scintillator (HEFS), Ce:LaGdCaSrBaF12 (Ce:LGCSB), in the form of bulk single crystals. The severe lattice distortion arising from multi-cation disorder induces exciton localization and effectively suppresses exciton diffusion. Through the rapid relaxation of localized excitons, the high-entropy Ce:LGCSB single crystals deliver a decay time of 1.23 ns with a 94.6% fast-component contribution and without any noticeable slow component. Through first-principles calculations, spectroscopic characterization, and transient dynamics analysis, we reveal that the ultrafast response originates from accelerated Frenkel exciton (FE) recombination enabled by the high-entropy environment. This work establishes entropy-engineered fluorides as promising ultrafast scintillator platforms and proposes a general strategy for extending sluggish diffusion effects to the excitonic scale, offering new opportunities for improving scintillation timing performance.
SCIENCE CHINA Materials•2026•DOI: 10.1007/s40843-025-3714-3
Eco-friendly aqueous zinc batteries (AZBs) are promising alternatives to lead-acid batteries in applications requiring both safety and energy density. However, their practical deployment is hindered by the synergistic deterioration of zinc anodes—structural collapse and kinetic failure—under high depth of discharge (DOD) and high current densities, which severely limits actual energy and power densities. Here, we report a strategy for the in situ integration of a double-layer topological chitosan framework (D-CTS) on current collectors via regulating phase separation kinetics during multistage coordination-neutralization electrophoresis. The vertical through-hole array is formed by coupling instantaneous and delayed phase separation. Subsequently, a columnar zinc array is mediated by D-CTS to construct an integrated component (D-CTS-Zn) comprising a vertical through-hole separator and an array anode. The embedded interconnected nanonetworks within the through-hole walls enable dynamic equilibrium of the columnar zinc array through a lateral ion compensation mechanism. As a result, Zn||Zn symmetric cells with D-CTS-Zn stably cycle over 3000 cycles at 200 mA cm−2 under 60% DOD. The assembled D-CTS-Zn||MnO2 battery delivers an energy density of 83 Wh kg−1 at an ultrahigh power density of 9.25 kW kg−1. This work provides a constructive strategy for chitosan phase separation regulation and separator-induced reversible metal array anodes.
New Carbon Materials•2026•DOI: 10.1016/S1872-5805(26)61094-3
Aqueous zinc-iodine (Zn-I2) batteries are promising for large-scale energy storage due to their intrinsic safety, low cost, and high theoretical capacity (211 mAh g−1 for iodine). However, their practical application is hindered by the poor electronic conductivity of iodine, sluggish redox kinetics, and the shuttle effect of polyiodides. This review systematically analyzes the reaction mechanisms of iodine cathodes, including two-electron (I−/I2) and multi-electron (I−/I2/I+ and I−/I2/I+/IO3−) pathways, and identifies key bottlenecks. It then comprehensively summarizes recent advances in iodine host materials, categorized into three strategies: physical confinement, chemical adsorption, and electrocatalysis. Representative host materials such as porous carbons, covalent organic frameworks (COFs), porous aromatic frameworks (PAFs), polymers, MXenes, and Prussian blue analogs (PBAs) are discussed, with emphasis on the structure–performance relationships. The review highlights that heteroatom doping (e.g., nitrogen) enhances chemical adsorption of iodine species, while single-atom catalysts (e.g., Co, Zn) provide electrocatalytic sites that accelerate conversion kinetics. Finally, future research directions are proposed, including exploration of multi-electron systems, mechanistic elucidation of iodine conversion, development of advanced host materials, and optimization of zinc anodes, to accelerate the commercialization of Zn-I2 batteries.
Journal of Fuel Chemistry and Technology•2026•DOI: 10.1016/S1872-5813(25)60619-0
Under the context of global energy transition and carbon neutrality, controlling nitrogen oxide (NOx) emissions from biomass combustion is of great significance, and the development of high-efficiency low-temperature catalysts has become a current research focus. In this study, Nb was used to dope and modify the Mn7-Cu3/BCN catalyst to construct the Mn7-Cu3-Nbx/BCN system. The doping amount was optimized through selective catalytic reduction (SCR) activity tests. The reaction mechanism was explored by combining in situ DRIFTS and density functional theory (DFT) simulations. Experimental findings revealed that the catalyst doped with 0.05% Nb achieved the optimal performance, sustaining a NO conversion efficiency of ≥94% within the temperature window of 150−275 °C while demonstrating improved resistance to alkali metal K poisoning. Mechanistic analyses showed that at low temperatures, the catalyst facilitated the SCR reaction via both the Eley-Rideal (E-R) and Langmuir-Hinshelwood (L-H) pathways, with the synergistic interaction between multiple active sites driving the efficient conversion of NH3 and NO. DFT calculations further confirmed that both pathways had the characteristics of low reaction energy barriers and significant exothermicity, ensuring the high activity and feasibility of the low-temperature reaction. The findings provided foundational theoretical support for the design of Nb-doped Mn-Cu-supported catalysts and the exploration of the underlying working mechanisms.
Environmental Chemistry•2026•DOI: 10.7524/j.issn.0254-6108.2025040202
Halophenols are highly toxic disinfection byproducts and common taste-and-odor pollutants in drinking water. In this study, a palladium catalyst confined within the pores of UiO-66 (Pd@UiO-66) was prepared via a double-solvent method and applied for the catalytic hydrodechlorination of 4-chlorophenol (4-CP). A surface-supported catalyst (Pd/UiO-66) was synthesized by deposition-precipitation as a benchmark. Comprehensive characterization using ICP-OES, XRD, TEM, EDX mapping, XPS, and in situ CO-IR revealed that Pd@UiO-66 exhibited smaller Pd particle sizes, higher Pd dispersion, and a greater proportion of cationic Pd species (Pdn+) compared to Pd/UiO-66. These features enhanced the activation and cleavage of the C–Cl bond. Catalytic tests demonstrated that Pd@UiO-66 achieved >90% removal of 4-CP within 15 minutes, with phenol as the sole degradation product, showing significantly lower predicted toxicity (ECOSAR) than the parent compound. The kinetics followed the Langmuir-Hinshelwood model. Pd@UiO-66 exhibited 2.1 times higher initial activity and 1.2 times higher turnover frequency than Pd/UiO-66. Moreover, the pore confinement effect imparted high stability, with no significant loss in initial activity (within 10%) after five reaction cycles. These results highlight the potential of confined Pd catalysts for efficient removal of halophenolic odorants from water.
SCIENCE CHINA Materials•2026•DOI: 10.1007/s40843-025-3999-x
The integration of photochromism (PhCh) and persistent luminescence (PersL) into a single material remains a formidable challenge due to the complex role of defects in modulating optical properties. Here, we employ structurally simple CsX (X = Cl, Br) nanocrystals (NCs) as a model system to elucidate the relationship between defects and optical behaviors. We demonstrate that CsX NCs accommodate two distinct types of chlorine vacancy defects upon X-ray irradiation: intrinsic vacancies from synthesis and X-ray-induced vacancies. This dual-defect engineering enables reversible blue coloration under X-ray irradiation (20–70 kV), attributed to recoverable chlorine vacancies that are rapidly eliminated by visible light within 30 s. The photochromic behavior exhibits excellent cycling stability with a color difference (ΔRL1) of 56.9% and a recovery rate (ΔRL2) of 98.1%. Furthermore, Br− incorporation deepens the energy level of intrinsic chlorine vacancies from 0.47–0.71 eV to 0.83 eV, resulting in intense persistent luminescence lasting over 30 minutes. These dual-mode PhCh–PersL characteristics position CsX NCs as promising candidates for X-ray colorimetric imaging and dynamic anti-counterfeiting applications. Our findings establish a defect-oriented design principle extendable to other halide systems, advancing the development of multifunctional photonic materials.
SCIENCE CHINA Materials•2026•DOI: 10.1007/s40843-025-3974-1
MAB-phase-derived compounds exhibit promising electromagnetic wave (EMW) absorption properties due to their unique layered structure and desirable physicochemical characteristics. Among them, Cr2AlB2 is particularly attractive owing to its excellent thermal and electrical conductivity. However, conventional synthesis of Cr2AlB2 requires inert gas protection to prevent oxidation, significantly increasing production costs and limiting its application in EMW absorption. To overcome this bottleneck, we report the successful synthesis of high-purity Cr2AlB2 in ambient air using the molten salt shielded synthesis (MS3) method. This approach not only isolates the material from oxygen interference but also reduces the synthesis temperature, offering a cost-effective and scalable route. The as-synthesized Cr2AlB2 exhibits outstanding EMW absorption performance: a minimum reflection loss (RLmin) of -42.10 dB at 12.6 GHz and a maximum effective absorption bandwidth (EABmax) of 3.44 GHz at a thickness of 1.9 mm. This work not only facilitates the large-scale production of Cr2AlB2 but also provides critical insights into its practical application as a high-performance EMW absorber.
SCIENCE CHINA Materials•2026•DOI: 10.1007/s40843-025-4051-x
Graphite lubricants are critical for high-quality and high-efficiency drawing of refractory metal wires, yet inadequate dispersion stability frequently challenges their practical application. Inspired by the bio-surfactant synergic mechanism that combines different bio-surfactants to collectively reduce surface energy and friction, a binary anionic surfactant system comprising sodium dodecyl benzene sulfonate (SDBS) and sodium lignosulfonate (SL) was engineered to enhance dispersion and stability via a synergistic effect. The synergistic parameter β was calculated to be −2.34, indicating strong synergism. The resulting graphite lubricants maintained homogeneous dispersion for up to 60 days. Molecular dynamics (MD) simulations combined with density functional theory (DFT) calculations confirmed that the synergistic effects originate from steric hindrance, electrostatic repulsion, π-π stacking, and hydrogen bonding. These hierarchical secondary interactions collectively increased the interfacial formation energy at the graphite/surfactant/water tri-phase interface, thereby effectively wetting particle powders and enhancing stability. During metal wire drawing, the graphite lubricants reduced the friction coefficient between the die and metal wires to 0.06, ultimately enabling drawn tungsten wires with superior surface integrity, expanded loop diameter, and enhanced tensile strength relative to single-surfactant benchmarks. This study provides experimental and theoretical guidance to design effective graphite lubricants for high-quality drawn metal wires.
SCIENCE CHINA Materials•2026•DOI: 10.1007/s40843-025-4104-4
Covalent organic frameworks (COFs) are promising adsorbents for gas adsorption and separation, yet identifying optimal structures among their vast design space requires efficient high-throughput screening. Conventional machine-learning predictors rely heavily on specific gas-related features, which are time-consuming and limit scalability, leading to inefficiency and labor-intensive processes. Here, we propose COFAP, a universal COFs adsorption prediction framework that extracts multi-modal structural and chemical features via deep learning and fuses these complementary features through a cross-modal attention mechanism. Without relying on explicit gas-specific thermodynamic descriptors, COFAP achieves state-of-the-art prediction performance on the hypoCOFs dataset under the conditions investigated, outperforming existing approaches. Based on COFAP, we found that high-performing COFs for gas separation concentrate within a narrow range of pore size and surface area. A weight-adjustable prioritization scheme is also developed to enable flexible, application-specific ranking of candidate COFs. Superior efficiency and accuracy render COFAP directly deployable in crystalline porous materials.