SCIENCE CHINA Materials•2026•DOI: 10.1007/s40843-025-3607-9
Enhancing light olefin selectivity and extending catalytic durability remain critical challenges for ZSM-5 zeolites in methanol-to-olefins (MTO) conversion, primarily due to inherent diffusion restrictions along the MFI b-axis and poor coke accommodation. Here, we report a hierarchically single-crystalline ZSM-5 sheet architecture featuring interconnected multiscale porosity and a remarkably reduced b-axis thickness (<50 nm), quantitatively verified by three-dimensional electron tomography. Real-time confocal laser scanning microscopy tracking demonstrated significantly enhanced molecular diffusivity compared to conventional micron-sized ZSM-5 (Micro-ZSM-5). This engineered structure distributes abundant aluminum sites on highly accessible diffusion pathways, achieving an enlarged coke accommodation of 16.31 wt% with a coke deposition rate of 0.59 mg g−1 h−1, only one third of that in Micro-ZSM-5. In continuous MTO operation, the hierarchical ZSM-5 sheet (Hier-ZSM-5-S) maintained an average ethylene and propene selectivity of 63.5% for 22.2 hours (WHSV = 3.6 h−1, T = 480°C), which was 19% higher and 6.5 times longer than Micro-ZSM-5, respectively. This hierarchically shortened b-axis structure establishes a generalizable paradigm for enhanced diffusion and coke accommodation in precisely designed pore systems, applicable to various reactions.
SCIENCE CHINA Materials•2026•DOI: 10.1007/s40843-025-3617-x
Macrophages are pivotal in infection resolution and tissue repair via dynamic M1-to-M2 phenotypic polarization. Although various nano-biomaterials can modulate macrophage polarization, achieving sequential M1-to-M2 transition using a single nanoformulation remains challenging. Here, we propose a strategy employing transition metal carbide/nitride (MXene) nanosheets, internalized by macrophages, as the sole regulator to induce sequential polarization. Under a rotating magnetic field, the high electrical conductivity and magnetoelectric activity of endocytosed MXene generate electrical signals and reactive oxygen species (ROS), driving M1 polarization. Upon magnetic field removal, the inherent bioactivity of MXene facilitates repolarization to the M2 phenotype. Mechanistically, this transition involves inhibition of the NF-κB signaling pathway and activation of the JAK-STAT signaling pathway. In vivo, MXene nanosheets under on-off rotating magnetic field stimulation enabled sequential M1-to-M2 polarization, promoting bacterial clearance and tissue regeneration in infected wounds. This two-step sequential strategy targeting macrophages offers a promising therapeutic approach for infected wound healing.
SCIENCE CHINA Materials•2026•DOI: 10.1007/s40843-025-3628-3
The solution aggregation structures of conjugated polymers are pivotal in determining their film morphology and optoelectronic properties, yet the relationship between solution aggregation and device performance remains elusive in organic photodiode (OPD) systems. Herein, we introduce the first examination of solution aggregation structures of all-polymer OPD blends, with a focus on how molecular entanglement modulates aggregation behavior and subsequent photodiode performance of low-cost poly(3-pentylthiophene). Using small-angle neutron scattering and freeze-dried imaging, we provide a comprehensive analysis of the solution-state aggregation behavior of poly(3-pentylthiophene) and its evolution in the blend, revealing profound impacts on film morphology and device performance. With finely optimized aggregation, the resulting all-polymer OPD achieves a record-high specific detectivity of ~4×10^13 Jones at zero bias, outperforming all bulk heterojunction (BHJ)-type self-powered OPDs reported to date. This device also demonstrates remarkable thermal stability, with negligible performance degradation after over 800 h of thermal annealing at 85 °C. Furthermore, the self-powered OPD exhibits excellent performance across a broad spectral range, enabling its application in both water quality monitoring and biosensing. This work offers new insights into the solution aggregation behavior of conjugated polymers in OPDs and highlights the importance of resolving solution aggregation in optimizing device function.
Journal of Environmental Engineering Technology•2026•DOI: 10.13205/j.hjgc.202605021
The digestate from anaerobic digestion of food waste is separated into solid residue and liquid filtrate. The filtrate retains high nutrient and carbon content, making it a viable resource for recovery. This study prepared biochar from food waste digestate residue and employed it as an electrode active material in a flow-electrode capacitive deionization (FCDI) system, with activated carbon as a control, to assess nitrogen and phosphorus removal from kitchen waste biogas slurry. ZnCl₂ modification significantly enhanced the biochar's specific surface area, adsorption capacity, capacitance, and conductivity. The optimal mass fraction of modified biochar in the electrode liquid was 7.5%. In simulated digestate, the FCDI system achieved removal efficiencies of 47.7% for NH₄⁺-N and 55.2% for reactive phosphorus (RP) over 12 hours. Performance ranking of electrode materials was activated carbon > ZnCl₂-modified biochar > unmodified biochar. In continuous operation with actual anaerobic digestion filtrate, maximum removal efficiencies were 32.2% for NH₄⁺-N and 26.2% for RP. The reduced performance in real digestate is attributed to organic foulants such as peptides and amino acids, which block ion-exchange membrane channels, increase membrane resistance, and impede ion transfer and charge transport, thereby diminishing deionization efficiency.
Journal of Environmental Engineering Technology•2026•DOI: 10.13205/j.hjgc.202605020
To address the high CO2 emission proportion in the industrial sector, distillers' grain waste was converted into biochar for CO2 adsorption from flue gas. Raw biochar suffers from weak pore adsorption and poor selectivity at elevated temperatures. This study employed ash self-templating and particle self-assembly to create hierarchical pores and simultaneously load amine groups onto distillers' grains-derived biochar, yielding amine-functionalized hierarchical porous carbon spheres. The amine loading significantly increased, providing more CO2 adsorption sites, while retaining macroporosity (total pore volume 0.0030–0.0066 cm3/g after amine loading), which enhanced morphological stability and CO2 mass transfer. The optimal sample, 0.2PW-K-CNF-PEI, exhibited a CO2 adsorption capacity of 1.03 mmol/g at 100 °C, a CO2 diffusion coefficient of 0.0495 min−1, and a selective adsorption capacity of 44 mg/g at 80 °C. This work offers a solution for valorizing distillers' grain by-products and capturing CO2 from low-temperature flue gas.
SCIENCE CHINA Materials•2026•DOI: 10.1007/s40843-025-3950-x
Photocatalytic oxygen reduction reaction (ORR) for hydrogen peroxide (H2O2) production via the two-electron pathway offers an environmentally friendly oxidant and a clean fuel. However, challenges exist in optimal oxygen (O2) adsorption capacities and maintaining O–O bond during O2 activation. Herein, we present a zinc single-atom catalyst (Zn/VN-CN) incorporating nitrogen vacancies (VN), designed to modulate the electronic structure of the photocatalyst, leading to optimized O2 adsorption energy and a remarkable enhancement in H2O2 yield. Benefiting from the synergistic effect between nitrogen vacancies and Zn single atoms, the optimized Zn/VN-CN catalyst exhibits a photocatalytic H2O2 production rate of 2.399 mmol g−1 h−1 under visible-light irradiation, representing a 12-fold enhancement compared to pristine g-C3N4 (CN), along with a high H2O2 selectivity of 87.4%. Combined experimental and theoretical studies indicate that the Zn-N3 sites act as highly active reaction centers, while nitrogen vacancies increase the charge density and downshift the d-band center of the Zn sites, thereby moderating O2 adsorption strength, lowering the activation energy barrier for the formation of *H2O2, and further converting it to H2O2. This work proposes an effective strategy for tuning O2 adsorption behavior to achieve highly selective and active photocatalytic H2O2 production.
SCIENCE CHINA Materials•2026•DOI: 10.1007/s40843-025-3918-x
Electrochemical seawater electrolysis powered by renewable energy is a highly promising route toward sustainable hydrogen production, mitigating both energy shortages and carbon emissions. However, chloride-induced corrosion and competitive chlorine evolution reactions lead to metal site dissolution, severely impairing durability, especially at industrial-level current densities. Here, we report a nitrite-incorporated cobalt-iron layered double hydroxide (CoFe-NO2−-LDH) electrocatalyst that exhibits exceptional activity and stability for seawater splitting. The nitrite anion acts as an electronic pump: it accepts electrons to facilitate the formation of high-valence Fe species essential for initial OER activation, and donates electrons under high potential to suppress oxidative dissolution. Moreover, the negatively charged nitrite generates an electrostatic repulsion field that effectively repels chloride ions, protecting metal active sites from corrosion and segregation. The in situ characterization confirms that nitrite doping weakens the Fe–O covalency, which suppresses lattice oxygen participation and promotes a stable adsorbate-evolving mechanism, consequently leading to significantly enhanced operational stability. When used as an anode, the CoFe-NO2−-LDH catalyst achieves over 1000 h of stable operation at 1000 mA cm−2 in seawater electrolysis, demonstrating great potential for practical applications.
SCIENCE CHINA Materials•2026•DOI: 10.1007/s40843-025-4097-3
The on-demand patterning of two-dimensional transition metal dichalcogenides (TMDs) with tailored edges is critical for electronic and optoelectronic applications but remains technically challenging. Here, we report a stress-guided anisotropic etching strategy for producing large-area, well-ordered MoS2 nanostructures, including nano-ribbons and nano-squares, without templates. By applying uniaxial cumulative stress followed by selective thermal etching, MoS2 monolayers are statistically etched into ribbon-like structures whose width inversely correlates with applied stress magnitude. The newly etched edges are macroscopically straight or serrated, predominantly Mo-zigzag terminated, and enhance photoluminescence by a factor of ~8.0. The edge type depends on the angle between stress direction and crystallographic orientation, corroborated by theoretical calculations. Biaxial stressing generates well-defined nano-squares, offering a scalable, versatile patterning route for engineering 2D materials with tailored functional edges, promising for electrocatalytic and optoelectronic applications.
SCIENCE CHINA Materials•2026•DOI: 10.1007/s40843-025-4014-3
Laser-induced graphene (LIG) methods, including photothermal and photochemical approaches, are promising for flexible electronics yet face distinct limitations. Photothermal methods often produce graphene with uncontrolled structural and functional properties, while photochemical methods are restricted to a narrow range of precursors. To address these limitations, we propose a pressure-driven LIG (P-LIG) method that uses transient laser-generated pressure fields as an additional control parameter to improve graphene quality. An integrated framework combining ultrafast pump–probe interferometric imaging, large-scale molecular dynamics (MD) simulations, and explainable artificial intelligence (XAI) was developed to investigate this approach. Time-resolved measurements reveal the generation of transient pressure fields during femtosecond laser irradiation of polyimide films, confirming pressure as an intrinsic feature of the process. MD simulations under controlled pressure conditions demonstrate that pressure promotes the nucleation and stacking of graphene layers, resulting in more continuous and planar graphitic networks. XAI analysis quantitatively identifies the important contributions of pressure. These results confirm that the transient pressure introduced by the P-LIG method plays a key role in promoting more ordered, continuous, and planar graphene networks, and enhancing structural integrity and material quality beyond traditional methods. This provides a practical pathway for improving the performance and reliability of LIG-based flexible electronic devices.