SCIENCE CHINA Materials•2026•DOI: 10.1007/s40843-026-4359-0
Organic solar cells (OSCs) require cathode interlayers (CILs) that combine high charge transport, defect passivation, and thickness insensitivity for scalable manufacturing. Here, we report the synthesis of a novel A-D-A-A'-type polymer, PDPP2F-NDI-N, via the green and efficient direct arylation polymerization (DArP) method. The multiple electron-deficient units in the backbone confer strong electron-withdrawing character, effective work function modulation, enhanced built-in potential, high crystallinity, and ordered molecular packing. PDPP2F-NDI-N exhibits a high electron mobility of 1.01 × 10⁻³ cm² V⁻¹ s⁻¹ and electrical conductivity of 3.13 × 10⁻³ S m⁻¹, facilitating efficient charge extraction and transport. Its interfacial modification capability suppresses interfacial defects and reduces non-radiative recombination losses. In ternary OSCs, PDPP2F-NDI-N achieves a high power conversion efficiency (PCE) of 20.44%, with outstanding thickness insensitivity retaining 92.8% of peak PCE at a 30 nm CIL thickness, and a T80 lifetime exceeding 1700 hours under photo-thermal aging. This work demonstrates that poly(A-D-A-alt-A') backbone design combined with DArP synthesis provides an effective strategy for developing high-performance, thickness-insensitive, and stable polymeric CILs, advancing efficient, stable, and scalable OSC applications.
SCIENCE CHINA Materials•2026•DOI: 10.1007/s40843-025-3774-3
Lithium-air capacitor batteries (LACBs) integrate the rapid charge-discharge capability of supercapacitors into conventional lithium-oxygen batteries, significantly enhancing power density. However, their cycling stability remains unsatisfactory. In this study, we incorporated redox mediators (RMs) into an LACB featuring a dual-cathode configuration. This design facilitates sustained electron transfer between the electrode and Li2O2/Oxygen, thereby delaying RM deactivation caused by electrode passivation and improving overall electrochemical performance. The RM-enhanced battery achieved over 250 cycles at 2 mA cm−2 with a limited capacity of 0.5 mAh cm−2, while exhibiting a 0.54 V reduction in charging voltage at 0.1 mA cm−2 compared to the RM-free system. Furthermore, application of an aluminum foil sealing technique enabled a power density of 13.8 mW cm−2 at 6 mA cm−2, overcoming mass transport limitations inherent in open-cell configurations. We also investigated the influence of oxygen barrier films with varying barrier capabilities on LACB performance. Results indicate that films with superior oxygen resistance better maintain a clean capacitor electrode surface, thereby providing more stable electron supply to the RMs and enhancing rate capability and cycling performance. These findings underscore the potential of redox mediators in improving the performance and longevity of LACBs, offering a promising strategy for their future development.
Chinese Journal of Environmental Engineering•2026•DOI: 10.12030/j.cjee.202511002
To treat large-air-volume, low-concentration volatile organic compounds (VOCs) containing tetrachloroethylene (PCE) generated from rubber-metal bonding, this study systematically investigated the adsorption-desorption behavior and interaction mechanisms of PCE, toluene, and methyl isobutyl ketone (MIBK) on granular activated carbon (GAC). Static adsorption experiments showed that PCE adsorption capacity reached 556.6 mg·g−1, while dynamic multi-component adsorption capacity was 179.6 mg·g−1. Kinetic analysis indicated that PCE adsorption was controlled by both intraparticle diffusion and external surface adsorption, whereas toluene and MIBK were primarily intraparticle diffusion-limited. During high-temperature nitrogen desorption, PCE underwent dechlorination, hydrogenation, and recombination, producing trichloroethylene, 1,2-dichloroethane, 1,2-dichloropropane, and HCl, with HCl accounting for 3.61% of the chlorine molar content in adsorbed PCE. After four adsorption-desorption cycles, the iodine value of GAC dropped below the industry standard of 600 mg·g−1; however, water washing and alkali immersion extended the cycle life to 8 and 9 cycles, respectively. The HCl generation pattern in co-adsorption systems was consistent with single-PCE systems. A regeneration process combining alkali immersion and water washing was proposed and integrated into an engineering strategy. Compared to conventional activated carbon adsorption coupled with RTO incineration, the proposed classification strategy reduced annual costs by 49.5×10⁴ CNY. This work provides a cost-effective and safe solution for Cl-VOCs treatment.