Environmental Chemistry•2026•DOI: 10.7524/j.issn.0254-6108.2025012901
N2O is a potent greenhouse gas, and its catalytic decomposition is of significant environmental importance. In this study, three CeO2 supports with different morphologies—nanorods (NR), nanocubes (NC), and nanooctahedra (NO)—were prepared via a hydrothermal method. Rh catalysts supported on these CeO2 materials were synthesized using a deposition-precipitation method, and their catalytic performance for N2O decomposition was evaluated. Results demonstrate that Rh/CeO2-NR exhibits superior catalytic activity compared to Rh/CeO2-NC and Rh/CeO2-NO under identical reaction conditions, including in the presence of O2 and H2O. Characterization reveals that Rh/CeO2-NR possesses abundant oxygen vacancies and a relatively high number of intrinsic defect sites, which facilitate the transfer of O intermediates. Additionally, Rh/CeO2-NR exhibits an appropriate Rh0/Rhn+ ratio, promoting the redox cycle between Rh species and reactants, thereby enhancing catalytic activity. The study underscores the critical role of CeO2 support morphology in optimizing Rh-based catalysts for N2O decomposition, offering a strategy to improve catalytic efficiency and stability for industrial applications.
SCIENCE CHINA Materials•2026•DOI: 10.1007/s40843-026-3961-8
This correction addresses an inadvertent misplacement of Fig. 4b3 during figure reorganization in the original article published in Science China Materials, volume 65, issue 10, 2022, page 2850 (DOI: 10.1007/s40843-022-2024-6). The corrected Fig. 4b is presented herein. The authors confirm that this correction does not affect the results, conclusions, text, or figure caption of the original work. The correction was requested by the authors and received on 6 January 2026, accepted on 8 January 2026, and published online on 10 February 2026. The original study introduced flexible electrostatic hydrogels derived from marine organisms for nitric oxide-enhanced photodynamic therapy against multidrug-resistant bacterial infections. The correction ensures the accurate representation of experimental data, maintaining the integrity of the scientific record.
SCIENCE CHINA Materials•2026•DOI: 10.1007/s40843-025-3966-0
The development of low platinum-loading catalysts for the economically viable hydrogen evolution reaction (HER) remains challenging. Herein, a precursor dilution strategy is used to fabricate Pt nanoclusters anchored on Ni-embedded porous carbon microspheres. The approach begins with the facile synthesis of Zn/Ni-based coordination polymers (Ni-BTC-Zn) due to the isomorphic substitution of Zn2+ and Ni2+. During pyrolysis, the evaporation of zinc species results in a highly porous carbon structure with well-dispersed nickel nanoparticles. Subsequent solvothermal treatment allows for the uniform deposition of Pt nanoclusters to form the final bimetallic PtNi catalysts (PtNi-BTC-C). Among them, the optimized PtNi-BTC-C10 exhibits exceptional alkaline HER performance, requiring an overpotential of only 41 mV to achieve 10 mA cm−2 and a low Tafel slope of 31.1 mV dec−1. It also demonstrates outstanding durability with a current retention of 90.7% after 70 h, far exceeding Pt/C. Extensive characterization confirms that moderate Zn dilution optimally modulates the Ni particle size and dispersion, leading to maximized active sites and enhanced charge transfer. Combined with DFT calculations, the Pt-Ni-cluster model for PtNi-BTC-C10 possesses an optimized electronic structure with a shifted d-band center, which facilitates water dissociation and optimizes H* desorption with the most favorable energetics (0.262 eV). This work provides a fundamental understanding of precursor dilution engineering and offers a versatile pathway for designing advanced noble-metal-based bimetallic electrocatalysts.
SCIENCE CHINA Materials•2026•DOI: 10.1007/s40843-026-4131-3
p-n heterojunction solar-blind photodetectors based on p-type materials and n-type Ga2O3 have attracted significant attention in optoelectronics due to their inherent low dark current and self-powered operation. Organic-inorganic hybrid heterojunctions integrating p-type organic materials with n-type Ga2O3 offer a promising solution to overcome lattice mismatch, enabling device performance breakthroughs. In this work, Ga2O3 thin films were treated via a supercritical fluid (SC) technique, which significantly reduced defect state density while improving crystallinity and surface uniformity, laying a foundation for heterojunction interface optimization. Simultaneously, a self-assembled monolayer (SAM) was introduced at the organic-inorganic heterojunction interface. The high-quality Ga2O3 surface engineered via SC treatment facilitated efficient, oriented self-assembly of SAM molecules, enabling precise modulation of interfacial energy band alignment and promoting separation and transport dynamics of photogenerated carriers. Benefiting from synergistic SC modification and SAM functionalization, the fabricated solar-blind photodetector achieved a highest responsivity of 111.7 mA/W and a specific detectivity of 1.02 × 10^11 Jones under zero bias (self-powered mode) and weak 254 nm light with an intensity of 5 μW/cm2. These results demonstrate a viable route to high-performance, self-powered solar-blind photodetectors through interface engineering.