New Carbon Materials•2026•DOI: 10.1016/S1872-5805(26)61117-1
Graphite-based bipolar plates (GBPs) are critical components in proton exchange membrane fuel cells (PEMFCs), offering excellent electrical and thermal conductivity, corrosion resistance, and durability. However, their inherent brittleness and porous structure lead to inadequate mechanical strength and high gas permeability, limiting practical application and large-scale manufacture. This review summarizes recent advances in GBP fabrication, focusing on the effects of graphite raw materials, polymer matrices, conductive and reinforcing fillers, and molding processes on GBP performance. The relationships among graphite particle size, morphology, surface characteristics, filler dispersion, interfacial bonding, resin content, and the electrical conductivity, mechanical strength, gas permeability, and corrosion resistance of GBPs are discussed. The effects of material composition, microstructure, and processing conditions on overall performance are analyzed. Trade-offs between electrical conductivity, mechanical strength, gas permeability, corrosion resistance, and processability are highlighted. Strategies for improving performance are summarized, including optimization of graphite raw materials, multiscale filler design, interfacial regulation, resin-content optimization, and improvements in molding processes.
Journal of Environmental Engineering Technology•2026•DOI: 10.13205/j.hjgc.202605007
Reservoirs are significant sources of nitrous oxide (N2O), a potent greenhouse gas. The nosZ-type denitrifying bacteria, which reduce N2O to inert N2, play a critical role in mitigating emissions. This study investigated the community structure, diversity, and abundance of nosZ-type denitrifiers in surface sediments (0-15 cm) from 18 reservoirs in the northeastern Qinghai-Tibet Plateau, including 10 in the Yellow River mainstem and 8 in the Huangshui River basin. Sampling occurred during dry (May 2023) and wet (August 2023) seasons. High-throughput sequencing of the nosZ gene and quantitative PCR were employed. Results showed that Proteobacteria dominated (78.91%). Paracoccus and Halomonas were biomarkers in the Yellow River mainstem. Diversity was significantly higher in the Huangshui basin (P<0.05), with no temporal difference. Gene abundance was higher in the Huangshui basin (165.24×10^5 copies/g) than in the Yellow River mainstem (34.43×10^5 copies/g), and higher in wet season (128.55×10^5 copies/g) than dry season (61.27×10^5 copies/g) (P<0.05). Redundancy analysis and hierarchical partitioning identified sediment temperature, pH, total phosphorus, and water total nitrogen as key drivers, explaining 17.14%, 16.89%, 13.83%, and 11.23% of community variation, respectively. These findings reveal significant spatiotemporal heterogeneity and provide a scientific basis for N2O mitigation in plateau reservoirs.
SCIENCE CHINA Materials•2026•DOI: 10.1007/s40843-025-4079-4
Utilization of ultrahigh-nickel LiNi_xCo_yMn_1-x-yO_2 (NCM) (x > 0.97) in Li-ion batteries can distinctively boost energy density through enhanced discharge capacity. However, capacity and thermal stability deteriorate as Ni content approaches the limit. Here, we propose a facile strategy by introducing high-valence tungsten (W) into ultrahigh-nickel polycrystalline LiNi_0.98Co_0.01Mn_0.01O_2 (PCNCM98). W-doped PCNCM98 (W-PCNCM98) exhibits refined, compactly stacked primary particles, whereas PCNCM98 shows equiaxial, non-uniform larger particles. The refined microstructure enhances mechanical strength: average particle hardness of W-PCNCM98 is 104 MPa, 1.5 times higher than PCNCM98 (68 MPa). This improved mechanical property suppresses lattice volume changes and relieves microcrack formation from H2–H3 phase transition. Consequently, cycling performance in pouch-type full cells is significantly enhanced, with capacity retention of 73% after 2000 cycles at 1 C and 25 °C, 54% higher than PCNCM98. Enhanced structural stability and strong electron affinity of W6+ also improve thermal stability: exothermic peak for W-PCNCM98 is postponed to 203 °C with heat generation of 1287 J g−1, versus 190 °C and 1528 J g−1 for PCNCM98. This high-valent doping strategy stabilizes ultrahigh-nickel NCM cathodes, accelerating large-scale EV applications.