SCIENCE CHINA Materials•2026•DOI: 10.1007/s40843-026-4405-9
Conventional metal-halide X-ray scintillators, including Bi4Ge3O12 (BGO), Cs(Na)I:Tl, and Lu1.8Y0.2SiO5:Ce (LYSO), suffer from hygroscopic decomposition, high-temperature fabrication, and mechanical rigidity, which restrict their deployment in harsh-environment radiography. This study reports a nontoxic zero-dimensional organic–inorganic hybrid copper(I) halide, Cu2I2(C26H36NP)2 (Compound G), synthesized via a room-temperature solution route. The bulky phosphine ligands confer exceptional superhydrophobicity, with the material retaining 91.95% of its initial luminescence after 30 days of water immersion. A flexible scintillator screen fabricated from styrene-ethylene-butene-styrene (SEBS) exhibits a light yield of ~32,500 photons MeV-1, a spatial resolution of 19.14 lp mm-1, and a detection limit of 0.8 μGyair s-1. The screen enables stable X-ray imaging under flexible, high-temperature, and underwater conditions, eliminating vignetting and distortion in nonplanar objects. These metrics demonstrate that the superhydrophobic copper(I) halide scintillator addresses the water-stability bottleneck of commercial scintillators while delivering competitive light output and resolution, offering a viable pathway for medical diagnosis, nondestructive inspection, security checking, and space exploration.
SCIENCE CHINA Materials•2026•DOI: 10.1007/s40843-026-4473-9
Selective ion separation is critical for resource recovery, water treatment, lithium extraction from salt lakes, and nuclear waste management, yet the differences in size, solvation structure, and coordination behavior among ions are often minimal, and separation is further complicated by valence, interfacial charge, and competing ions. Nanoporous materials with tunable sub-nanometer channels and chemically active interfaces can regulate ion entry, solvation reorganization, interfacial partitioning, intrapore migration, and release. This review examines three mechanistic categories—size and solvation sieving, chemical recognition, and dynamic gating—from the perspective of confined transport and ion–pore interactions, and compares their roles and coupling in systems of monovalent–monovalent, divalent–divalent, heterovalent, and chemically similar multivalent ions. We further distinguish selective adsorption, membrane enrichment, and transmembrane transport, and discuss how selectivity definitions, ion flux, feed composition, driving force, and operating time affect performance evaluation. Current research faces three major challenges: lack of comparability of performance data across different test conditions, insufficient direct evidence of ion solvation, site occupancy, and migration under operating conditions, and the complexity of feed streams. By adopting a sequential ion transport process as a unified conceptual framework, this review systematically compares separation mechanisms across diverse nanoporous materials, including MOFs, COFs, zeolites, 2D materials, microporous polymer membranes, ion-exchange membranes, biomimetic nanochannels, organic–inorganic composites, functionalized porous carbons, and biochars. This transport-process-oriented framework provides a general and mechanistic perspective for understanding and comparing selective ion separation across diverse nanoporous platforms.
SCIENCE CHINA Materials•2026•DOI: 10.1007/s40843-025-3771-9
High-entropy carbonitride ultra-high temperature ceramics (HECN-UHTCs) typically require high densification temperatures, leading to grain coarsening and degraded mechanical properties. This study introduces CrSi2 as a sintering additive for (Ti, Zr, Hf, Nb, Ta)(C, N), effectively reducing the densification temperature by 200 °C. During sintering, interdiffusion and cation exchange result in the formation of an orthorhombic (Ti, Zr, Nb)2Cr4Si5 phase within the ceramic matrix. The resulting dual-phase ceramic exhibits a hardness of 24.65 ± 0.23 GPa and a fracture toughness of 6.03 ± 0.48 MPa m1/2, significantly surpassing most reported HECN-UHTCs. Enhanced mechanical properties are attributed to crack deflection, increased localized lattice strain, and Cr grain boundary segregation. This liquid phase-assisted low-temperature sintering strategy offers a promising pathway for densifying other ultra-high temperature ceramics.
SCIENCE CHINA Materials•2026•DOI: 10.1007/s40843-025-3547-7
Inorganic perovskite solar cells (IPSCs) have attracted significant attention due to their excellent light and thermal stability and potential in tandem applications. However, their efficiency and stability are often limited by residual lattice stress and defects at interfaces and within the bulk, causing severe nonradiative recombination. Here, we introduce a zero-dimensional supramolecular complex, (ETP)2SbCl5, as a dual-interface and bulk modifier to regulate CsPbI3 film growth. The modifier exhibits spatial segregation: ETP+ cations anchor at the buried interface, passivating defects on TiO2 and perovskite surfaces; Sb3+ and Cl− ions diffuse into the bulk during annealing, relieving residual stress; and Cl− accumulates on the top surface, passivating cation defects. Consequently, the modified CsPbI3 solar cell achieves a power conversion efficiency (PCE) of 21.71% and an open-circuit voltage (VOC) of 1.27 V, retaining 97.4% of initial efficiency after 500 h of maximum power point (MPP) tracking. This work demonstrates a synergistic strategy to simultaneously address interfacial and bulk defects, advancing high-performance and stable inorganic photovoltaics.
SCIENCE CHINA Materials•2026•DOI: 10.1007/s40843-025-3883-2
Tensile stress annealing (TSA) is an effective strategy for tailoring magnetic anisotropy and high-frequency performance in nanocrystalline soft magnetic alloys. Here, we systematically investigate the influence of TSA on the microstructure, magnetic domain evolution, and permeability stability of Fe69.5Co3Nb2Mo1.5Si14B9Cu1 nanocrystalline alloys. Across all applied stresses (0–300 MPa), the alloys retain an ultrafine grain size (≤11 nm), yet the induced uniaxial anisotropy constant (Ku) rises sharply from 22.5 to 665 J/m3. This increase in Ku refines the magnetic domain structure, reducing average domain width from 110 to 36 μm, and shifts the magnetization mechanism from domain-wall displacement to rotation-dominated reversal. Quantitative correlation between Ku, domain structure, and effective permeability (μe) reveals that higher stress suppresses μe at low frequencies but yields exceptional frequency stability: μe ≈ 2330 is maintained up to 1 MHz at 50 MPa, and μe ≈ 585 remains constant from 1 kHz to 10 MHz at 300 MPa. These findings demonstrate that stress-induced anisotropy is a decisive factor in governing high-frequency magnetic response, offering both mechanistic insight and a practical framework for designing next-generation soft magnetic materials for precision current transformers, EMC filters, and MHz-class power electronics.
Chinese Journal of Environmental Engineering•2026•DOI: 10.12030/j.cjee.202508047
Selective recovery of aluminum compounds from fly ash is a key route for its high-value utilization. This study developed a multi-stage activation process for extracting Al(OH)3 from fly ash, comprising mechanical activation, calcination activation, chemical separation, and carbonation precipitation. Fly ash was mixed with carbide slag and CaF2, then calcined; the resulting clinker was leached with Na2CO3 solution to extract Al. The CaO generated from high-temperature calcination of carbide slag facilitated the separation of Si and Al. After solid-liquid separation, CO2 was introduced into the Al-rich leachate to precipitate Al(OH)3. The process promoted the formation of Ca12Al14O32F2 and inert Ca2SiO4, achieving efficient Si-Al separation during calcination. Under optimal conditions (mechanical activation for 60 min, 4% CaF2, calcination at 1000°C for 2 h, leaching with 40 g/L Na2CO3), the Al extraction rate reached 91.8%, and the product purity was 98.9%. The alumina extraction residue exhibited porous and highly reactive characteristics, suitable for producing flame-retardant materials or high-value silicon-based products (e.g., white carbon black, molecular sieve adsorbents). The process offers a promising industrial route for fly ash valorization, with potential integration with cement production lines for synergistic CO2 capture and utilization.
Journal of Environmental Engineering Technology•2026•DOI: 10.13205/j.hjgc.202605012
The extraction process of large-scale infiltration galleries significantly alters surface water-groundwater exchange dynamics. Existing models often simplify the gallery as a boundary condition or adopt loosely coupled schemes, constrained by iterative exchange algorithms, failing to capture dynamic water flux interactions and transient responses. This study focuses on the large riverbed infiltration and purification water supply project in Shijiazhuang, China, establishing an integrated three-domain fully coupled numerical model—encompassing surface water, groundwater, and the infiltration gallery—using the dual-node coupling approach in HydroGeoSphere. The model sets two upstream inflow scenarios (wet and dry seasons) and simulates groundwater level evolution and water exchange processes under two operational modes: single-pump extraction at 1000 m³/h and no pumping. Results show that groundwater levels decline markedly under pumping, with the most pronounced response in the dry season, where maximum drawdown reaches approximately 1.24 m. Monitoring wells near the gallery show an earlier hydraulic response to pumping, reaching peak drawdown rates about 2–3 days sooner than wells farther away. At steady-state balance, surface water contributes more recharge to groundwater during the wet season than in the dry season, and water exchange between the gallery and aquifer is substantially enhanced under pumping. Spatially, water exchange concentrates primarily around transverse and longitudinal gallery sections, consistent with localized permeability enhancement from the perforated structure. These findings reveal groundwater dynamics and multi-domain interaction mechanisms under operational conditions, providing a theoretical basis for planning, design, and management of similar riverbed infiltration projects.
SCIENCE CHINA Materials•2026•DOI: 10.1007/s40843-025-3842-8
The metal-support interactions (MSIs) play a significant role in regulating the electronic structure of metal species on oxide; however, they are often overlooked on carbon-based supports. In this work, hollow nitrogen-doped carbon (H-NC) supported Ru nanoparticles catalyst (Ru/H-NC) was prepared by a solvothermal method using H-NC as support and RuCl3 as precursor. Subsequently, Ru/H-NC was annealed at different temperatures (Ru/H-NC t °C) to adjust the effect of MSIs between H-NC support and Ru nanoparticles. The X-ray photoelectron spectroscopy results showed that the MSIs between Ru species and H-NC support increased with the increase of temperature, and more electrons were transferred from Ru species to H-NC support, thus regulating the valence state of Ru. In hydrogen evolution reaction (HER), the as-synthesized Ru/H-NC 300 °C merely requires overpotential of 35.45 mV to achieve 10 mA/cm2 at low Ru mass loading of 24.03 μg/cm2 on the glassy carbon electrode. The cyclic voltammetry test revealed that the electrochemically active surface area increased first and then decreased with the increasing MSIs. Moreover, electrochemical impedance spectroscopy results showed that HER kinetics of Ru/H-NC t °C catalysts increased first and then decreased with the MSIs enhancement. The density functional theory calculations confirmed that the MSIs effectively optimize the adsorption strength of the key intermediates (H*, HO*) on Ru clusters, and thus greatly improve the catalytic performance of Ru/H-NC in HER.
SCIENCE CHINA Materials•2026•DOI: 10.1007/s40843-025-4079-4
Utilization of ultrahigh-nickel LiNi_xCo_yMn_1-x-yO_2 (NCM) (x > 0.97) in Li-ion batteries can distinctively boost energy density through enhanced discharge capacity. However, capacity and thermal stability deteriorate as Ni content approaches the limit. Here, we propose a facile strategy by introducing high-valence tungsten (W) into ultrahigh-nickel polycrystalline LiNi_0.98Co_0.01Mn_0.01O_2 (PCNCM98). W-doped PCNCM98 (W-PCNCM98) exhibits refined, compactly stacked primary particles, whereas PCNCM98 shows equiaxial, non-uniform larger particles. The refined microstructure enhances mechanical strength: average particle hardness of W-PCNCM98 is 104 MPa, 1.5 times higher than PCNCM98 (68 MPa). This improved mechanical property suppresses lattice volume changes and relieves microcrack formation from H2–H3 phase transition. Consequently, cycling performance in pouch-type full cells is significantly enhanced, with capacity retention of 73% after 2000 cycles at 1 C and 25 °C, 54% higher than PCNCM98. Enhanced structural stability and strong electron affinity of W6+ also improve thermal stability: exothermic peak for W-PCNCM98 is postponed to 203 °C with heat generation of 1287 J g−1, versus 190 °C and 1528 J g−1 for PCNCM98. This high-valent doping strategy stabilizes ultrahigh-nickel NCM cathodes, accelerating large-scale EV applications.
Environmental Chemistry•2026•DOI: 10.7524/j.issn.0254-6108.2025042802
Activated carbon, characterized by its extensive pore structure, high specific surface area, and superior adsorption capacity, is widely employed in advanced water treatment. However, upon reaching adsorption saturation, its efficacy diminishes, necessitating replacement or regeneration. Thermal regeneration stands out due to its high desorption efficiency, simple equipment requirements, and low energy consumption, making it the predominant industrial method. Despite its prevalence, systematic investigations into the underlying reaction mechanisms and the influence of operational parameters remain insufficient. This review comprehensively examines common thermal regeneration technologies for saturated activated carbon, including multi-hearth furnaces, rotary kilns, superheated steam, microwave, and solar regeneration. It delineates the fundamental principles, process flows, advantages, disadvantages, and current research status of each method. The desorption and reaction mechanisms of pollutants within activated carbon pores during thermal regeneration are discussed in detail, along with the effects of critical conditions such as temperature, atmosphere, and purge gas flow rate on pollutant removal efficiency. Furthermore, the relationship between activated carbon performance parameters and regeneration efficiency is analyzed, and innovations based on conventional thermal regeneration, as well as integration with emerging technologies, are explored. Finally, the challenges facing thermal regeneration are summarized, and future research priorities are proposed, focusing on the treatment of waste gas and liquid byproducts, technology integration, and enhancement of overall regeneration performance. This review aims to provide a scientific foundation for the sustainable recycling of activated carbon in industrial applications.