Strength and Microstructural Characteristics of Sludge Solidified by Loess-Based Composite Solidifying Agent
To address land waste and poor bearing capacity from sludge landfill, this study developed a composite solidifying agent using loess, fly ash, desulfurized gypsum, and cement. Orthogonal experiments combined strength testing, SEM/XRD microanalysis, permeability and heavy metal leaching tests, and cost accounting. Results show that cement significantly enhances early and mid-term strength, while loess dominates later strength development. Optimal fly ash and desulfurized gypsum content is 12% each. The optimal mix ratio (loess:fly ash:desulfurized gypsum:cement:sludge) is 0.1:0.12:0.12:0.08:1. The solidified matrix forms dense structures via C-S-H gel and ettringite (Aft), effectively controlling heavy metal leaching at low cost. This work enables solid waste resource utilization and provides robust support for sludge solidification engineering.