New Carbon Materials•2026•DOI: 10.1016/S1872-5805(26)61109-2
Silicon-carbon (Si/C) composites are promising high-capacity anode materials for next-generation lithium-ion batteries, but their commercialization is hindered by severe volume expansion during cycling. We report a chemical vapor deposition method using the pyrolysis of silane, in which ultrafine nano-Si enters a porous carbon framework to produce kilogram-scale Si/C composites. The carbon framework with abundant micropores (~1.9 nm) confines the amorphous silicon and accommodates the volume changes of nano-Si during both lithiation and de-lithiation. The resulting Si/C composites have a 56.76% Si content and have a specific capacity of 2179 mAh g–1, a high initial Coulombic efficiency (ICE) of 93.5%, and a low specific surface area (1.32 m2 g–1). In addition to the nanoconfinement effect, the median particle size (D50, 7.3-13.0 μm) of the carbon framework was shown to control the mechanical strength, coating uniformity and Li+ transport. A D50 of 8.2 μm endows the Si/C composites with outstanding comprehensive properties. They have an excellent rate performance with a 97.0% retention at 3 C relative to 0.1 C, show only minor variations in ICE difference at 60 ℃/-20 ℃ compared with room temperature, and have a low expansion of 35.8% from the delithiated to the lithiated state. The composite was then mixed with graphite to prepare the anode, which was then paired with an NCM523 cathode to assemble pouch cells. The pouch cell retained 87.46% of its initial capacity after 1000 cycles at 1 C. Because of the low expansion of the electrode, the material avoids structural degradation during cycling and thus has an excellent long-term stability.
Environmental Chemistry•2026•DOI: 10.7524/j.issn.0254-6108.2025010201
The Guanzhong region, traversed by the Wei River Basin, is one of the most industrially, agriculturally, and medically advanced and densely populated areas in Northwest China, has seen increasing attention paid to the pollution of perfluoroalkyl substances (PFASs) in its surface water environment. This study systematically investigated the pollution characteristics of PFASs in the surface water of this region and their ecological and health risks. By optimizing the online solid-phase extraction-liquid chromatography-tandem quadrupole mass spectrometry (Online SPE-LC/MS/MS), efficient detection of 19 PFASs was achieved, with the method detection limits ranging from 0.2 ng·L−1 to 0.3 ng·L−1, linear correlation coefficients all ≥ 0.990, and spiked recoveries between 75.2% and 130.0%. Monitoring data indicated that PFBA, PFPeA, PFHxA and PFOS, short-chain perfluorinated compounds, were the main pollutants in this region, with high detection frequencies and concentrations, but the overall content was lower than that in most areas of China. The concentrations of PFASs in surface water showed significant seasonal variations, with the highest concentrations during the dry season (∑19PFASs:126.1 — 2584.3 ng·L−1), followed by the normal season (∑19PFASs:3.5—3567.6 ng·L−1), and the lowest during the wet season (∑19PFASs:26.3—294.6 ng·L−1). Ecological risk assessment showed that, except for PFDoDA in the dry season, the ecological risk quotient (RQ) of all other PFASs was < 1. Although the water of the Wei River is not used as direct drinking water, health risk assessment indicated that all PFASs posed low risks, with only PFOA and PFOS showing potential risks (HR > 0.1) to adults and children at some sites during dry/normal seasons. This study provides a scientific basis for PFASs pollution control in the Wei River Basin.
SCIENCE CHINA Materials•2026•DOI: 10.1007/s40843-025-3952-5
High-entropy alloys (HEAs) and metallic glasses (MGs) are promising electrocatalysts but suffer from inherent limitations: HEAs lack corrosion resistance and uniform surfaces due to their crystalline nature, while MGs have limited compositional flexibility, restricting active-site diversity and electronic-structure tuning. High-entropy metallic glasses (HEMGs) integrate the structural disorder of MGs with the multi-principal-element chemistry of HEAs, offering a unique combination of robust corrosion resistance, homogeneous surfaces, and abundant tunable active sites. Using Pd20Pt20Cu20Ni20P20 as a model HEMG, we investigate its electrocatalytic performance for alcohol oxidation and hydrogen evolution. The HEMG exhibits superior activity and stability compared to conventional HEAs and MGs, attributed to its disordered structure and high configurational entropy, which promote optimized adsorption energies and accelerated charge transfer. This work bridges the performance gap between HEAs and MGs, demonstrating HEMGs as multifunctional electrocatalytic materials with potential for industrial applications.
Journal of Fuel Chemistry and Technology•2026•DOI: 10.1016/S1872-5813(26)60653-6
Carbon deposition caused by mass transfer limitations is a key challenge for traditional microporous ZSM-5 zeolites in coal tar catalytic cracking. To address this, benzene was used as a model compound. Parent ZSM-5 (NL-ZSM-5) was modified with tetraethylammonium hydroxide (TEAOH) to prepare hierarchical ZSM-5 zeolites with different mesopore sizes. Characterization (XRD, FT-IR, BET, TEM) confirmed successful mesopore introduction via selective desilication while retaining the MFI structure. At TEAOH concentration of 0.4 mol/L (ZSM-5-C), total pore volume increased from 0.24 to 0.43 cm3/g, and Brønsted acid amount increased from 0.28 to 0.67 mmol/g, with improved acid site accessibility. Catalytic experiments and carbon deposition analysis showed that hierarchical pore structure inhibits coking via a synergistic effect of diffusion enhancement and adsorption-site regulation. The coke amount of ZSM-5-C was 4.0%, only one-third of that of NL-ZSM-5 (11.9%). Molecular dynamics simulations confirmed that the diffusion coefficient of benzene in a 3.0 nm mesopore model is an order of magnitude higher than in a 2.0 nm model. Adsorption capacity decreases with increasing mesopore size, shortening residence time. Increasing temperature enhances diffusion but exponentially intensifies surface condensation reactions (Arrhenius effect), which dominates coke formation; hierarchical pores mitigate this negative effect. This research provides a theoretical basis for designing high-efficiency, coke-resistant catalysts for coal tar conversion.
SCIENCE CHINA Materials•2026•DOI: 10.1007/s40843-025-4018-6
The pursuit of advanced wear-resistant materials for cryogenic applications is often hindered by a fundamental trade-off between enhancing strength and damage tolerance. CoCrNi-based medium-entropy alloys (MEAs), while excellent in cryogenic toughness, suffer from this very limitation. Although second-phase reinforcement boosts strength, the strain incompatibility between phases inevitably triggers cracking, which is severely exacerbated at low temperatures. This work introduces a novel microstructural design strategy based on regulated partial recrystallization to overcome this long-standing challenge. By tailoring the thermomechanical processing of a (CoCrNi)90Mo10 MEA, we engineered a unique architecture where a fully recrystallized FCC phase is homogeneously embedded within a continuous skeleton of a hard, non-recrystallized σ phase. The alloy with this optimized microstructure achieved a remarkably low wear rate at 113 K that is less than half of its as-cast and fully recrystallized counterparts. The experimental and modeling results indicate the underlying synergy: the σ skeleton provides robust structural support and distributes stress deeply, while the recrystallized FCC phase, with its high density of grain boundaries and annealing twins, acts as a compliant strain-accommodating medium, effectively suppressing interfacial cracking. This combined 'skeleton effect' and 'recrystallization effect' not only delivers exceptional cryogenic wear resistance but also offers a practical strategy for designing high-performance, crack-resistant dual-phase composites for extreme environments.