SCIENCE CHINA Materials•2026•DOI: 10.1007/s40843-026-4249-2
Underwater bubble manipulation is critical for water electrolysis, heat transfer, and mineral flotation, yet existing strategies relying on buoyancy or Laplace gradient forces from asymmetric surface geometries suffer from limited flexibility and narrow applicability. This work introduces a temperature-responsive anisotropic cilia surface (TRAS) that achieves bidirectional long-range bubble transport by modulating elastic modulus and stiffness. The TRAS enables precise control over the asymmetric three-phase contact line and viscous resistance, facilitating reversible bubble motion. Experimental validation using aqueous ethanol droplets with varying surface tensions (73.16 mN/m for 0 vol% to 22.27 mN/m for 100 vol%) on cilia with center-to-center spacings of 0.2–1.0 mm reveals that transport direction depends on both cilia spacing and liquid surface tension. Droplets of 0 vol% and 20 vol% ethanol exhibit sustained reverse transport on hard cilia, while 60 vol%, 80 vol%, and 100 vol% solutions show sustained forward transport. Notably, 40 vol% ethanol droplets display bidirectional transport at 0.6 mm spacing, reverse transport at 0.8 and 1.0 mm, and forward transport at 0.2 and 0.4 mm. These results demonstrate that tuning surface tension and cilia spacing provides a versatile platform for directional bubble manipulation, with promising applications in heat transfer, electrochemistry, and gas handling systems.
Chinese Journal of Environmental Engineering•2026•DOI: 10.12030/j.cjee.202507088
Methanol is highly biodegradable, yet its efficient and stable anaerobic treatment is constrained by prolonged microbial adaptation to toxic substances, narrow microbial community structure, and poor sludge granulation. This study applied two functional additives—sodium bicarbonate (NaHCO3) as an inorganic carbon source (IC) and an amino-acid-rich organic functional supplement (FS)—to accelerate the startup of two upflow anaerobic sludge blanket (UASB) reactors. UASB-A received 3,000 mg·L−1 NaHCO3 and 127 mg·L−1 FS, while UASB-B received only 3,000 mg·L−1 NaHCO3. Both additives enabled rapid startup and granulation by shortening hydraulic retention time (HRT) and increasing organic loading rates (4, 6, 9, 15, 20, and 30 g COD·L−1·d−1). Granulation was evidenced by increased total suspended solids (TSS), volatile suspended solids (VSS), and particle size distribution. Microbial community analysis at HRT 0.2 d revealed highest relative abundances of Acetobacterium at 30.2% (UASB-A) and 36.9% (UASB-B). NaHCO3 supplementation enhanced syntrophy between Acetobacterium and the acetoclastic methanogen Methanothrix, while FS significantly increased the abundance of Sporomusa, establishing a novel syntrophic relationship with Methanothrix. These interactions promoted sludge granulation. The study demonstrates that functional additives facilitate rapid startup and granulation in methanol anaerobic treatment, offering a strategy to overcome process bottlenecks.
Environmental Chemistry•2026•DOI: 10.7524/j.issn.0254-6108.2024042404
The direct catalytic decomposition of the greenhouse gas N2O into nitrogen and oxygen holds significant environmental importance. In this study, CaO-modified Rh-based catalysts were prepared via a stepwise impregnation method. The catalyst structures were characterized, and their catalytic performances for N2O decomposition were investigated. The characterization results demonstrate that CaO doping significantly enhances catalytic activity and water resistance. Specifically, the 0.5Rh/Al2O3 catalyst exhibited a N2O conversion below 5% at 300 °C, whereas the 0.5Rh-4Ca/Al2O3 catalyst achieved 50% conversion under identical conditions, indicating markedly improved low-temperature activity. Compared to the undoped catalyst (0.5Rh/Al2O3), CaO doping (0.5Rh-xCa/Al2O3) strengthens metal-support interactions, improves Rh dispersion on the support surface, and modulates the electron density around Rh, thereby substantially boosting N2O decomposition capability. The catalyst also demonstrated excellent stability, maintaining essentially constant conversion over 40 h of reaction. These findings underscore the potential of alkaline earth metal oxide doping as an effective strategy for designing high-performance noble metal catalysts for N2O abatement.
SCIENCE CHINA Materials•2026•DOI: 10.1007/s40843-025-3835-0
The development of high-performance CO2 separation membranes is critical for advancing carbon capture technologies. Two-dimensional (2D) material membranes, with tunable interlayer nanochannels functionalized by nanomaterials (e.g., metal ions), are promising for CO2 capture. However, achieving uniform nanomaterial distribution without compromising separation performance remains a challenge. Here, we propose a multifunctional molecular immobilization strategy to fabricate a metal ion intercalated graphene oxide (GO) membrane with enhanced CO2 capture performance. The multifunctional molecule sodium p-aminobenzenesulfonate (SPABS) enables in situ and uniform distribution of Na+ in the interlayer channels of the GO membrane. The amino groups of SPABS undergo nucleophilic addition reactions with epoxy groups on GO sheets, resulting in stable interlayer channels. Meanwhile, the hydrophilic sulfonic acid groups enhance water adsorption capacity in the GO interlayer channels, synergizing with Na+ to form active sites that facilitate fast and selective transport of CO2 over N2. The resulting membrane exhibits enhanced CO2 capture performance. A large-sized membrane (15 cm × 20 cm) fabricated by scalable blade-casting shows reproducible performance. This work provides insights and a tool for tailoring nanochannels of 2D material membranes for molecular separation.