SCIENCE CHINA Materials•2026•DOI: 10.1007/s40843-026-4249-2
Underwater bubble manipulation is critical for water electrolysis, heat transfer, and mineral flotation, yet existing strategies relying on buoyancy or Laplace gradient forces from asymmetric surface geometries suffer from limited flexibility and narrow applicability. This work introduces a temperature-responsive anisotropic cilia surface (TRAS) that achieves bidirectional long-range bubble transport by modulating elastic modulus and stiffness. The TRAS enables precise control over the asymmetric three-phase contact line and viscous resistance, facilitating reversible bubble motion. Experimental validation using aqueous ethanol droplets with varying surface tensions (73.16 mN/m for 0 vol% to 22.27 mN/m for 100 vol%) on cilia with center-to-center spacings of 0.2–1.0 mm reveals that transport direction depends on both cilia spacing and liquid surface tension. Droplets of 0 vol% and 20 vol% ethanol exhibit sustained reverse transport on hard cilia, while 60 vol%, 80 vol%, and 100 vol% solutions show sustained forward transport. Notably, 40 vol% ethanol droplets display bidirectional transport at 0.6 mm spacing, reverse transport at 0.8 and 1.0 mm, and forward transport at 0.2 and 0.4 mm. These results demonstrate that tuning surface tension and cilia spacing provides a versatile platform for directional bubble manipulation, with promising applications in heat transfer, electrochemistry, and gas handling systems.
SCIENCE CHINA Materials•2026•DOI: 10.1007/s40843-025-3547-7
Inorganic perovskite solar cells (IPSCs) have attracted significant attention due to their excellent light and thermal stability and potential in tandem applications. However, their efficiency and stability are often limited by residual lattice stress and defects at interfaces and within the bulk, causing severe nonradiative recombination. Here, we introduce a zero-dimensional supramolecular complex, (ETP)2SbCl5, as a dual-interface and bulk modifier to regulate CsPbI3 film growth. The modifier exhibits spatial segregation: ETP+ cations anchor at the buried interface, passivating defects on TiO2 and perovskite surfaces; Sb3+ and Cl− ions diffuse into the bulk during annealing, relieving residual stress; and Cl− accumulates on the top surface, passivating cation defects. Consequently, the modified CsPbI3 solar cell achieves a power conversion efficiency (PCE) of 21.71% and an open-circuit voltage (VOC) of 1.27 V, retaining 97.4% of initial efficiency after 500 h of maximum power point (MPP) tracking. This work demonstrates a synergistic strategy to simultaneously address interfacial and bulk defects, advancing high-performance and stable inorganic photovoltaics.
Journal of Fuel Chemistry and Technology•2026•DOI: 10.3724/2097-213X.2025.JFCT.0031
The high-temperature behavior of biomass ash critically influences gasifier operational efficiency. This study investigates the differential high-temperature behaviors of corn straw ash (CSA) and wheat straw ash (WSA) using an intelligent ash fusion analyzer, high-temperature rotating viscometer, X-ray diffraction (XRD), SEM-EDS, and FactSage thermodynamic simulations. Both ashes contain high K2O (>30%) and exhibit flow temperatures below 1300 °C. Despite higher K2O and lower SiO2, CSA exhibits a higher flow temperature (1241 °C) than WSA, attributed to elevated CaO (10.39%) and MgO (7.33%) that promote formation of high-melting silicates (K2MgSiO4, K2Ca2Si2O7, CaSiO3). In contrast, WSA with lower CaO (4.92%) and MgO (2.82%) tends to form low-melting potassium silicates. At high temperatures, both slags are typical crystalline slags, with viscosity rising sharply below a critical temperature. For CSA, rapid nucleation and coarsening of silicate crystals (e.g., KAlSiO4 grain size increases from 20.5 nm at 1350 °C to 192.9 nm at 1050 °C) cause abrupt viscosity increase. For WSA, a high P2O5 content (10.05%) induces a 'chemical dilution effect', leading to persistent KAlSiO4 during cooling and elevated viscosity, especially at the final cooling stage. This study elucidates how ash chemical composition governs high-temperature phase equilibrium and non-equilibrium kinetics, thereby macroscopically affecting ash fusion and rheological behavior, providing a theoretical basis for deeper understanding of biomass ash high-temperature characteristics.
SCIENCE CHINA Materials•2026•DOI: 10.1007/s40843-026-4072-3
All-inorganic, hole-transport-material-free (HTM-free), carbon-based perovskite solar cells (C-PSCs) have attracted significant attention due to their exceptional stability and low cost. However, their performance and commercial potential are constrained by poor interfacial contact, insufficient crystallinity, and energy level misalignment. In this work, we address these challenges via a molecular engineering strategy by introducing tetrakis(4-ethynylphenyl)methane (TEPM) as a multifunctional additive. The alkynyl moiety (C≡C) in TEPM coordinates with Pb2+ ions in perovskite precursors, synergistically slowing crystallization kinetics to regulate crystal growth and passivate deep-level defects. Consequently, CsPbI3 films exhibit larger grain sizes, improved crystallinity, and lower defect densities. Devices modified with TEPM achieved a record power conversion efficiency (PCE) of 20.01% (certified 19.58%). Additionally, unencapsulated devices retained 87.6% of their initial efficiency after 1080 h under ambient conditions (25 °C, 30% relative humidity), and maintained 94.0% of their initial efficiency after 730 h of continuous AM 1.5G illumination in air. This work sets a new efficiency benchmark for inorganic HTM-free C-PSCs and provides a versatile molecular engineering strategy for developing high-performance, stable perovskite photovoltaics.